Materials Science Forum 649
05/2010
10.4028/www.scientific.net/MSF.649.493
Aluminio, Ana Fernandez, Andrea Niklas, I+D+i, Jacques Lacaze, Materiales ligeros, Tecnologías de fundición
Both thermal analysis (TA) and differential thermal analysis (DTA) have been used since long to evaluate latent heat release and solid fraction evolution during solidification of metallic alloys. TA makes use of cooling curves recorded under «natural» cooling while DTA consists in recording the temperature difference between the sample temperature and an inert reference during a controlled cooling, i.e. at imposed constant cooling rate. In both cases, the solid fraction evolution is deduced from a calculation of the latent heat release as estimated by means of a heat transfer model. This paper provides a comparison of such evaluations performed on one Al-Si alloy.
Ana Isabel Fernández Calvo (AZTERLAN), Andrea Niklas (AZTERLAN), Jacques Lacaze (CIRIMAT)
¿Cómo podemos ayudarte?.
Mantente informad@ de la actividad de AZTERLAN.
Mantente informad@ de la actividad de AZTERLAN.
Formamos equipos de trabajo en distintos ámbitos de la metalurgia y los procesos de transformación de metales.
Indícanos los datos de tu trabajo y nos pondremos en contacto contigo lo antes posible.
Comparte tu reto con nuestro equipo. Hablar no puede más que acercarnos un poco más a posibles soluciones.