Microstructure and Mechanical Properties of a New Secondary AlSi10MnMg (Fe) Alloy for Ductile High Pressure Die Casting Parts for the Automotive Industry
Primary AlSi10MnMg alloy is the most widely used alloy for manufacturing of vacuum assisted high pressure die castings
Austempered Ductile Iron (ADI) Alternative Material for High-Performance Applications
Austempered ductile iron (ADI) grades are standardized, and the requirements of current international standards (EN 1564-12/ASTM A897-15) are
Chunky graphite formation in ductile cast irons: Effect of silicon, carbon and rare earths
Use of rare earths, high silicon and carbon contents, and low cooling rates are reported as possible reasons
On the Crystallization of Compacted and Chunky Graphite from Liquid Multicomponent Iron-Carbon-Silicon-Based Melts
Extensive SEM work was carried out on deep-etched specimens to reveal the evolution of compacted and chunky graphite
Active Mg Estimation Using Thermal Analysis: A Rapid Method to Control Nodularity in Ductile Cast Iron Production
Appropriate nodularity in ductile iron castings is strongly associated with the presence of high enough not combined Mg
Understanding Superfine Graphite iron solidification through interrupted solidification experiments
The tensile strength of near-eutectic gray iron can be increased from 230–300 to 300–345MPa, without a significant increase
Effect of solution heat treatment on gas porosity and mechanical properties in a die cast step test part manufactured with a new AlSi10MnMg(Fe) secondary alloy
The effect of heat treatment on gas porosity and mechanical properties was investigated in a step test part
Investigation of Thermal and Mechanical Properties of Quenchable High-Strength Steels in Hot Stamping
The interfacial heat transfer coefficient (IHTC) is determined in the industrial range of contact pressure applied during the
A new secondary AlSi10MnMg (Fe) Alloy suitable for manufacturing of ductile Aluminium parts by vacuum assisted high pressure die casting technology
Vacuum assisted high pressure die castings (VPDC) with high ductility requirements are usually manufactured with primary AlSi10MnMg alloy.
High performance cast parts. Advanced feeding systems for metallurgical optimization
Foundry sector, as a whole, has incorporated relevant technological advances into productive processes. Nevertheless, the specific field of
Solidification of Superfine Graphite Iron Revealed by Interrupted solidification Experiments
The tensile strength of near-eutectic grey iron can be increased from 230–300 to 300–345 MPa, without a significant
On the Nucleation of Graphite in Lamellar Graphite Cast Iron
Extensive research on graphite nucleation in lamellar graphite irons was conducted over the years, with many theories, more
On the crystallization of graphite from liquid iron-carbon-silicon Melts
Extensive SEM work was carried out on deep etched specimens to reveal the evolution of graphite shape in
Statistical study to determine the effect of carbon, silicon, nickel and other alloying elements on the mechanical properties of as-cast ferritic ductile irons
There is a great interest in fully ferritic ductile irons due to their structural homogeneity, remarkable ductility and
Procedure for predicting the mechanical properties of pieces obtained by casting
Procedure that enables future mechanical properties to be determined based on real-time observation of the process variables; that
Understanding compacted graphite iron solidification through interrupted solidification experiments
While the manufacture of compacted graphite (CG) iron castings has seen significant expansion over the recent years, the